ZIF-8 derived hollow CuO/ZnO material for study of enhanced photocatalytic performance
摘要： Tetracycline hydrochloride (TC) is a broad-spectrum antibiotic extensively used in medical and veterinary fields. However, its excess harms the environment and human health. Recently, construction of CuO/ZnO heterojunctions has a very good effect in the treatment of organic matter in water. In this study, we used zeolite imidazolate framework (ZIF-8) as initial material to synthesize porous and hollow CuO/ZnO photocatalysts for catalytic degradation of TC. The results show that the synthesized CuO/ZnO has the characteristics of porous hollow polyhedron when the molar ratio of Cu and Zn is 0.1. Obviously, photocatalytic degradation rate was better comparing to CuO/ZnO nanoparticles as well as pure ZnO and CuO particles, respectively, which could reach 87% at 60min under visible light (λ>420 nm) and has good stability. Porous hollow CuO/ZnO composites are very promising for effective and environmentally friendly degradation of tetracycline hydrochloride in water.
关键词： Photocatalysis,Tetracycline hydrochloride,Zeolite imidazolate frameworks (ZIF-8),Hollow CuO/ZnO
更新于2025-11-14 17:04:02
-
Ultraviolet photodetectors using hollow p-CuO nanospheres/n-ZnO nanorods with a pn junction structure
摘要： We report on ultraviolet (UV) photodetectors with a pn junction structure consisting of hollow p-CuO (h-CuO) nanospheres and n-ZnO nanorods (NRs). To form the pn junction structure, thermal annealing was conducted using a transferred monolayer of Cu-ion-incorporated polymer spheres onto the n-ZnO NRs/n-Si substrate. Device performance was evaluated by comparing the effects of h-CuO nanosphere coverage changed by sphere shrinkage during thermal annealing of Cu-ion-incorporated polymer spheres. Three samples were prepared by varying the transfer times of h-CuO on ZnO NRs: 0 times (Reference), 1 time (CZ-I), and 2 times (CZ-II). The CZ-II-based UV detector shows a fast rising time of 1.8 s and a falling time of 0.26 s, which are faster rising by 2.2 and 1.3 times and faster falling by 3.1 and 32.6 times than those of the CZ-I and Reference UV detectors, respectively, under illumination with UV light at 254 nm. Moreover, the On/Off current ratio of the CZ-II UV detector is 4.58, which is about 3.3 times and 3.5 times higher than that of the CZ-I and Reference devices, respectively. The higher h-CuO coverage on the ZnO NRs that form the pn junction structure can effectively separate the electron and hole and suppress recombination by mutual transfer of photo-generated electrons and holes in the heterojunction.
关键词： Hollow CuO,ZnO,UV detector,transfer of spheres monolayer
更新于2025-09-23 15:19:57