[IEEE 2019 34th Symposium on Microelectronics Technology and Devices (SBMicro) - Sao Paulo, Brazil (2019.8.26-2019.8.30)] 2019 34th Symposium on Microelectronics Technology and Devices (SBMicro) - MOS solar cells for indoor LED energy harvesting: influence of the grating geometry and the thickness of the gate dielectrics

摘要： This paper discusses the metal-oxide-semiconductor (MOS) solar cells for energy harvesting from indoor illumination using Al/SiO2/Si-p structures. Wafers of the Si-p (100) with a resistivity of 10 Ω.cm were used. The gate dielectric was grown by rapid thermal processing (RTP) with thicknesses of 1.65, 1.73, 2.10 and 2.23 nm. The main parameters studied were extracted using electrical characterization through IxV curves of the MOS solar cells with total areas of 3.24 cm2. At first, it was observed an increase of the dark current density from 0.49 to 4.4 μA/cm2 for the thickness varying from 1.65 to 2.23 nm. It is worthy of note the increase of the generated power from 8.1 to 46.7 μW/cm2 with the rise of the thickness in the range of 1.65 to 2.23 nm for a constant incident power of 5 mW/cm2. In this case, the lower the thickness, the higher the tunneling current through the gate dielectrics, which causes the decrease of the depletion region length and this decrease, in turn, makes the generation current density lower in the depletion region. Also, the reduction of the short-circuit current (JSC) due to the increase of the widths (W) and spacings (S) of the fishbone-grating geometry was well-correlated with the decrease of the perimeter (Pe) and the rise of the aspect ratio W/S.