Stable and durable laser-induced graphene patterns embedded in polymer substrates
摘要： The stability and durability of laser-induced graphene (LIG) patterns embedded in polymer substrates are significant for their practical application. However, most of currently reported LIG precursors are facing the dilemma of weak structural controllability, poor resistance to acid/base, or bad processability. In this work, we efficiently converted the synthesized poly(Ph-ddm) into LIG using a straightforward CO2 laser, aiming to find a potential LIG precursor with excellent durability under harsh conditions. The graphene structure of obtained LIG was confirmed by Raman spectra, scanning electron microscope (SEM), transmission electron microscope (TEM) and X-ray photoelectron spectroscopy (XPS). Results indicated that the poly(Ph-ddm)-based LIG showed a low sheet resistance of 35 ?/sq as well as a high specific surface area of 883 m2/g. And due to the superior properties of poly(Ph-ddm), the LIG patterns exhibited excellent resistance to strong acid/base solutions and high adhesion on the substrate, which ensured their stable application under severe conditions. Besides, potential application of as-prepared LIG was demonstrated in well-performed supercapacitors and electrode for water splitting in an alkaline medium. Based on the results in this work, polybenzoxazine could be a promising precursor for stable and durable LIG preparation.
关键词： electrode for water splitting,laser-induced graphene,durability,supercapacitor,Polybenzoxazine
更新于2025-09-19 17:13:59
-
Form-stable benzoxazine-urethane alloys for thermally reversible light scattering materials
摘要： Thermally reversible light scattering (TRLS) materials based solely on benzoxazine-urethane (BA-a/PU) alloys were successfully fabricated and demonstrated in this work. The alloys displayed the opaque state below 40 °C. The alloys were transformed to the transparent state upon exposing to the transition temperature of 60–130?°C, depending on the molecular weights and mass concentrations of urethane prepolymers in the BA-a/PU alloys. The optical state transitions were reversible with small hystereses. BA-a/PU alloys exhibited a good optical contrast with 0%T at the light scattering state and almost 100%T at the transparent state. The alloys were glassy and form-stable up to 250?°C, due to the synergistic behavior in the glass transition temperatures. The reaction-induced phase separation effectuated by the incorporation of urethane prepolymer into thermosetting polybenzoxazine, the sizes and local concentrations of the phase-separated urethane microdomains in the supporting polybenzoxazine matrix, and the reversible dissolution and demixing of urethane microdomains and polybenzoxazine phase played crucial roles on TRLS properties of the developed benzoxazine-urethane alloys.
关键词： smart polymers,urethane,polymer blends and alloys,polybenzoxazine,thermally reversible light scattering