Evolution of the Structure and Properties of High-Chromium Heat-Resistant VZh159 Alloy Prepared by Selective Laser Melting: Part II
摘要： The evolution of the structural-phase state of the VZh159 alloy fabricated by selective laser melting after various types of thermal exposure and hot isostatic pressing (HIP) is studied. The effect of a long 500-h exposure at temperatures of 800 and 900°C on the phase composition and morphology of structural components is determined. The short-term and long-term strength of the material in various conditions are studied. It is shown that the segregation of dispersed particles of the σ phase after the gas-static treatment followed by aging and after prolonged exposure at high temperatures does not have a significant negative effect on the plastic and strength characteristics of the alloy. The long-term strength of the synthesized metal after the 500-h exposure at a temperature of 900°C corresponds to the certified values for the deformed semifinished product of the VZh159 alloy.
关键词： boride,heat treatment,σ-phase,HIP,gas-static treatment,VZh159,selective laser melting (SLM),transmission electron microscopy,cellular structure
更新于2025-09-19 17:13:59
-
Evolution of the Structure and Properties of High-Chromium Heat-Resistant VZh159 Alloy Prepared by Selective Laser Melting: Part I
摘要： The evolution of the structural-phase state of the VZh159 alloy fabricated by selective laser melting after various types of thermal exposure and hot isostatic pressing (HIP) is studied. The effect of a long 500-h exposure at temperatures of 800 and 900°C on the phase composition and morphology of structural components is determined. The short-term and long-term strength of the material in various conditions are studied. It is shown that the segregation of dispersed particles of the σ phase after the gas-static treatment followed by aging and after prolonged exposure at high temperatures does not have a significant negative effect on the plastic and strength characteristics of the alloy. The long-term strength of the synthesized metal after the 500-h exposure at a temperature of 900°C corresponds to the certified values for the deformed semifinished product of the VZh159 alloy.
关键词： σ phase,VZh159,HIP,heat treatment,boride,transmission electron microscopy,gas-static treatment,selective laser melting (SLM),cellular structure
更新于2025-09-19 17:13:59