Novel Ca2GdTaO6:Mn4+,M (M = Li+, Na+, K+, and Mg2+) red phosphors for plant cultivation light-emitting diodes: Synthesis and luminescence properties
摘要： Recently, Mn4+-activated red phosphors are becoming potential color converters for application in indoor plant cultivation light-emitting diodes, owing to their satisfactory luminescence properties as well as low cost. Herein, novel Mn4+-activated double perovskite-type Ca2GdTaO6 phosphors have been synthesized by a high-temperature solid-state reaction method in air, which exhibited a broad excitation band with two peaks locating at 355 nm and 496 nm in range of 250-600 nm and had an intense red emission peaking at 676 nm due to Mn4+:2Eg→4A2g spin-forbidden transition ranging from 650 to 750 nm under 355 nm excitation. Concentration-dependent luminescence properties were studied. The optimal Mn4+ doping concentration in Ca2GdTaO6 host was 0.004, and the concentration quenching mechanism was determined to be a dipole-dipole interaction among Mn4+ ions. Furthermore, the Ca2GdTaO6:0.004Mn4+ phosphor possessed the internal quantum efficiency up to 33% when excited at 355 nm. Besides, the decay lifetimes of Ca2GdTaO6:Mn4+ presented a reasonable downward trend with increasing Mn4+ concentration. In addition, the effect of charge compensation (co-doping of Li+, Na+, K+, and Mg2+ ions) on the luminescent properties of Ca2GdTaO6:Mn4+ phosphors was also investigated.
关键词： Indoor plant cultivation,Ca2GdTaO6,Mn4+,Double perovskite,Luminescence properties,Red phosphor
更新于2025-11-20 15:33:11
-
A novel double-perovskite LiLaMgTeO6: Mn4+ far-red phosphor for indoor plant cultivation white LEDs: Crystal and electronic structure, and photoluminescence properties
摘要： Deep-red-emitting Mn4t activated oxide phosphors are the hot research topic due to their potential applications in indoor plant cultivation LEDs. In this paper, a novel double-perovskite LiLaMgTeO6:Mn4t phosphor was firstly prepared by high-temperature solid-state reaction method and its structure of the phosphor was determined by X-ray diffraction (XRD) and Rietveld refinement. Density functional theory (DFT) calculations using VASP provide an insight into the bandgap and electronic structures of the LiLaMgTeO6 host. Under UV or blue excitation, LiLaMgTeO6:Mn4t shows a good stability and bright far-red light in the 540e800 nm range with the maximum at 708 nm, which matches well with the absorption band of phytochrome PFR, indicating its potential application in improving plant growth. The optimal Mn4t doping concentration was approximately 0.6 mol%. Furthermore, a white-LEDs device made of a 365 nm chip coated with present phosphor and commercial green, blue phosphors was designed for indoor plant cultivation. The results indicate that the LiLaMgTeO6: Mn4t phosphor possesses great application prospect in white-LEDs for plant cultivation.
关键词： Far red emission,Phytochrome,Double perovskite,LEDs,Thermal stability,Indoor plant cultivation