Effects of MgO Nanocrystal Powder on Long-Term Sustain and Address Discharge Characteristics in ac-Plasma Display Panel

摘要： We investigated the characteristics of MgO surface with MgO nanocrystal powders due to the long-term (500 hours) ion bombardment comparing with the conventional MgO surface in this study. When the MgO nanocrystal powders were coated on the conventional MgO surface, it was observed that the sputtered Mg particles from MgO surface were re-deposited on the MgO nanocrystal powders, which was able to significantly suppress the re-crystallization on the phosphor layers. We confirm that the MgO nanocrystal powders play a significant role in suppressing the degradation of the MgO surface and phosphor layer after long-term severe ion bombardments. Accordingly, when the MgO nanocrystal powers were applied to the conventional MgO surface, the variations of discharge characteristics, such as address discharge delay time, firing voltage of sustain and address discharge, and luminance, were significantly reduced comparing with the conventional MgO surface.