Tunable optical and magnetic properties of Ni-doped CuSe nanowires using AAO template assisted hydraulic method
摘要： High uniformity of un-doped and Ni-doped CuSe nanowires have been fabricated through smelting the bulk and injecting the melted liquid into the anodic aluminum oxide (AAO) template. The Ni dopant concentration and morphology of CuSe nanowires can be well controlled via preparing the bulk materials and the channel size of AAO template. The cathodoluminescence (CL) peaks of the un-doped, 0.5 at% and 1.0 at% Ni-doped CuSe nanowires showed a redshift of about 26 nm and 42 nm from un-doped CuSe nanowires (579 nm), respectively. Furthermore, above room temperature ferromagnetism was observed in 1.0 at% Ni-doped CuSe nanowires at 300 K. The facile injection molding method fabricated nanowires with tunable optical and magnetic properties could be applied to prepare varied nanomaterials for spintronic devices in the further.
关键词： optical,anodic aluminum oxide (AAO),CuSe,doped,nanowires,magnetic
更新于2025-11-14 17:03:37
-
Sol-Gel Template Synthesis and Characterization of Lu2O3:Eu3+ Nanowire Arrays
摘要： Uniform Lu2O3:Eu3+ nanowire arrays were successfully prepared by the sol-gel process using anodic aluminum oxide (AAO) templates. The as-synthesized nanowires are homogeneous, highly ordered, and dense and have a uniform diameter of ~300 nm defined by the AAO templates. The X-ray diffraction and selected area electron diffraction results show that the Lu2O3:Eu3+ nanowires have a polycrystalline cubic structure, and the crystallite size of the Lu2O3:Eu3+ nanowires is confined by the AAO template. The nanowires within the AAO template showed good photoluminescence and X-ray-excited optical luminescence performances for Lu2O3:Eu3+. The emission peaks were attributed to the 5D0 → 7FJ transitions of Eu3+ (J = 0, 1, 2, 3).
关键词： sol-gel method,nanowire arrays,Lu2O3:Eu3+,anodic aluminum oxide (AAO)