摘要： Porphyrin dyes have been widely used for the fabrication of efficient dye-sensitized solar cells (DSSCs). However, dye aggregation and charge recombination still exert negative effects on photovoltaic performance, resulting in unsatisfactory power conversion efficiencies (PCE). Herein, we report a new class of porphyrin sensitizers XW52 and XW53 employing four benzyloxy groups to wrap the porphyrin cores. As a result, an efficiency of 7.6% was obtained for XW52, with Voc and Jsc of 668 mV and 16.63 mA cm-2, respectively. Compared with XW52, an additional 2,6-dialkoxyphenyl group has been introduced to the N-atom of the phenothiazine donor to furnish XW53 with the aim to further improve the anti-aggregation character and the solubility, and thus the Voc was improved to 674 mV, and a higher efficiency of 7.9% was achieved for XW53. Upon cosensitization with PT-C6, the Voc and Jsc were synergistically enhanced to 727 mV and 18.67 mA cm-2, respectively. As a result, a high efficiency of 9.6% was successfully achieved for the cosensitization system of XW53 + PT-C6. These results provide an effective novel strategy for designing efficient porphyrin dyes by introducing multiple benzyloxy groups to the meso-phenyl groups.