摘要： Novel Bi3t, Eu3t co-doped Gd2GeO5 (GGO) phosphors were prepared by a high-temperature solid-state reaction method. X-ray diffraction, photoluminescence (PL), CIE chromaticity coordinates, internal quantum efficiency (IQE), and temperature-dependent PL spectra were applied to analyze the as-obtained phosphors. The emission spectra of the GGO:Bi3t, Eu3t phosphors showed both a broad blue band of Bi3t ions emission centered at 453 nm and the characteristic sharp red emission lines of Eu3t ions, corresponding to the 3P1→1S0 allowed transition of the Bi3t ions and the 5D0→7FJ (J ? 0, 1, 2, 3, 4) transitions of the Eu3t ions, respectively. Notably, the as-prepared GGO:Bi3t, Eu3t phosphors exhibited color-tunable emissions from blue (Bi3t) to red (Eu3t) with increasing the Eu3t doping concentration via a high-efficiency energy transfer process. Moreover, the mechanism of energy transfer from Bi3t to Eu3t ions was determined to be the dipole-quadrupole interaction. Impressively, the optimal GGO:0.05Bi3t, 0.12Eu3t phosphors had an outstanding IQE as great as 88% and good thermal stability. All these meaningful results demonstrated that blue-red color-tunable GGO:Bi3t, Eu3t phosphors have potential applications in white light-emitting diodes (LEDs) and plant growth LEDs.