摘要： In this paper it was investigated the combined effect of gold nanoparticles and high-pressure densification on the luminescence of Pr3+ doped heavy metal GeO2-PbO photonic glass. Localized states related to ion-trapped exciton defects, S1 and S2, were observed at 342 and 412 nm before densification. After densification under 7.7 GPa the structure of the glass host changed irreversibly, as indicated by the infrared spectrum, refractive index and density measurements. TEM analyses indicated that the high-pressure densification induced the formation of clusters of gold nanoparticles. The modifications observed in the absorption and luminescence spectra of Pr3+ ions in the VIS-NIR range were associated to the changes in the local field surrounding the Pr3+ ions in the host glass induced by high-pressure. For excitation at 445 nm (luminescence from 3P2) and 593 nm (luminescence from 1D2), the combined effect of densification and gold nanoparticles induced an increase in the emission band at 1050 cm-1. For excitation at 488 nm (luminescence from 3P0), the combined effect resulted in a strong decrease in the emission intensities in the VIS, revealing the emergence of non-radiative processes in resonance with 3P0 state. The observed behavior was probably due to energy transfer, ion trapped exciton defects and cross-relaxation processes among the Pr3+ ions and gold nanoparticles.