摘要： A series of Tm3+/Ho3+ sensitized 65GeO2-7BaF2-10B2O3-4Al2O3-4ZnO2-10Na2O glass samples were synthesized by using high temperature melting method. The spectral properties were systematically studied when Ho3+ concentration was 0.1, 0.3, 0.5 mol % and Tm2O3 changed from 0.3 to 2.5 mol %. Differential thermal analysis showed that ?T was higher than 190 oC, which illustrated this kind of matrix glass have better thermal stability. The absorption cross section peak height, free energy of Ho3+ from 5I8 to 5I7 and emission cross section were calculated according to Mc-Cumber theory. Under the excitation of 808 nm laser diode, fluorescence intensity at 1954 nm reached the highest value when the concentration of Ho3+ was 0.1 mol % and Tm3+ was 0.7 mol %. However the fluorescence intensity reduced greatly when Ho3+ concentration was 0.5 mol % and Tm3+ exceeded 1.5 mol %. The sensitized function and influence of different Tm3+/Ho3+ doped ion ratios on the spectral properties was studied.