Adsorption and Photocatalytic Decomposition of Gaseous 2-Propanol Using TiO2-Coated Porous Glass Fiber Cloth
摘要： Combinations of TiO2 photocatalysts and various adsorbents have been extensively investigated for eliminating volatile organic compounds (VOCs) at low concentrations. Herein, TiO2 and porous glass cloth composites were prepared by acid leaching and subsequent TiO2 dip-coating of the electrically applied glass (E-glass) cloth, and its adsorption and photocatalytic ability were investigated. Acid leaching increased the specific surface area of the E-glass cloth from 1 to 430 m2/g while maintaining sufficient mechanical strength for supporting TiO2. Further, the specific surface area remained large (290 m2/g) after TiO2 coating. In the photocatalytic decomposition of gaseous 2-propanol, the TiO2-coated porous glass cloth exhibited higher adsorption and photocatalytic decomposition ability than those exhibited by the TiO2-coated, non-porous glass cloth. The porous composite limited desorption of acetone, which is a decomposition intermediate of 2-propanol, until 2-propanol was completely decomposed to CO2. The CO2 generation rate was affected by the temperature condition (15 or 35 °C) and the water content (2 or 18 mg/L); the latter also influenced 2-propanol adsorption in photocatalytic decomposition. Both the conditions may change the diffusion and adsorption behavior of 2-propanol in the porous composite. As demonstrated by its high adsorption and photocatalytic ability, the composite (TiO2 and porous glass cloth) effectively eliminates VOCs, while decreasing the emission of harmful intermediates.
关键词： air purification,composite,adsorption,microporous material,porous glass,photocatalyst,TiO2
更新于2025-11-19 16:51:07
-
Influence of the Tb3+ concentration on the luminescent properties of high silica glass
摘要： Tb3+- doped high silica glass was prepared by sintering porous glass. The density, valence state and amount of Tb, transmittance, photoexcitation spectra, photoluminescence spectra, and cathodoluminescence spectra (CL) were recorded and the luminescence decay kinetics analyzed in details. These results show that the doping concentration in high silica glass is in direct proportion to the concentration in solution, and the density increases with the increasing concentration of rare earth ions as well as the intensity of emission spectrum. The largest emission intensity of 0.2 mol/L is more than 2 times higher than the intensity of the 0.05 mol/L. Besides, the “red” shift phenomenon could be distinguished clearly in the transmittance spectra. There is a broad band at the “red” region in the CL spectra. The decay time which is in the millisecond range in di?erent spectral range were measured and analyzed revealing that the decay time of 5D3 is shorter than that of 5D4.
关键词： Luminescent properties,Rare earth ions,High silica porous glass