Tailoring the collagen film structural properties via direct laser crosslinking of star-shaped polylactide for robust scaffold formation
摘要： Application of restructured collagen-based biomaterials is generally restricted by their poor mechanical properties, which ideally must be close to those of a tissue being repaired. Here, we present an approach to the formation of a robust biomaterial using laser-induced curing of a photosensitive star-shaped polylactide. The created collagen-based structures demonstrated an increase in the Young’s modulus by more than an order of magnitude with introduction of reinforcing patterns (from 0.15±0.02 MPa for the untreated collagen to 51.2±5.6 MPa for the reinforced collagen). It was shown that the geometrical configuration of the created reinforcing pattern affected the scaffold’s mechanical properties only in the case of a relatively high laser radiation power density, when the effect of accumulated thermomechanical stresses in the photocured regions was significant. Photo-crosslinking of polylactide did not compromise the scaffold’s cytotoxicity and provided fluorescent regions in the collagen matrix, that create a potential for noninvasive monitoring of such materials’ biodegradation kinetics in vivo.
关键词： mechanical properties,collagen,reinforcements,photopolymerization,biocompatible polymers,riboflavin
更新于2025-11-21 11:24:58
-
Electrochemical synthesis of Al–Al <sub/>2</sub> O <sub/>3</sub> composites for selective laser melting
摘要： Novel electrochemical method for obtaining Al–Al2O3 composites for selective laser melting technology has been studied. The electrochemical cell with the flexible cathode and the anode device has been developed. The initial aluminum powder was characterized: aluminum content was more than 99.8 wt %; the average particle diameter was ～40 μm. Oxidized aluminum powder was studied: γ–Al2O3 in the surface oxide layer form was detected; the increase in the particle diameter was 10–20 μm. Electrochemical oxidation technological parameters have been studied. At 0.1 A cm cathodic current density electrolysis duration was 220 min, 24 V voltage along with 80 ° C electrolyte temperature reached. The oxidation mechanism of aluminum particles has been developed. The increase in the surface oxide layer occurred, and this led to an increase in voltage. The 3D object from the oxidized aluminum powder was synthesized by selective laser melting method. The 3D object was perfectly sintered and did not crumble. Good reinforcements distribution in the volume of the synthesized 3D object has been achieved.
关键词： reinforcements,anodic oxidation,electrolysis,aluminum–alumina composites,selective laser melting
更新于2025-11-21 11:24:58