Synthesis of Nanocrystalline SnxCd1?xS Thin Films Capped with Thioglycerol and Methanol (TGM) and Study of Optical and Structural Properties
摘要： Nanostructured CdS (nCdS) and ternary SnxCd1?xS thin films capped with thioglycerol and methanol in 1:1 ratio in aqueous medium were prepared using hydrated stannous chloride (SnCl2·2H2O), anhydrous cadmium acetate (CH3COO)Cd·2H2O and thiourea (CS(NH2)2) as sources of Sn, Cd and S ions, respectively. Thickness of the film drastically decreases for low concentrations (0–2%) of Sn doping, then increases for (2–3%) and 5% Sn doping. Effects of Sn concentration variation on the optical properties, photoluminescence and structural properties of the nanoparticles were studied. The optical transmittance measurement using ultraviolet–visible–near infrared spectroscopy showed more than 80% transparency in the wavelength range 450–800 nm for 3% and 5% Sn doping. The direct optical band gap value of nanoCdS thin films was obtained as 2.91 eV, which decreased with Sn doping for its varying concentrations. Photoconductivity gain was negligible. A decrease in intensity of lower wavelength emission at 430 nm in nCdS was observed to have (2–5)% Sn content. X-ray diffraction patterns and selected area electron diffraction patterns confirmed formation of the nanocrystalline hexagonal CdSnS phase. Scanning electron microscope and transmission electron microscope measurements of the CdSnS thin films show that the particle size lies well under 20 nm.
关键词： SEM,TEM,photoluminescence,Optical study,XRD
更新于2025-11-21 11:18:25
-
Optical study of twin-tanked ICS solar heaters combined with asymmetrical CPC-type reflectors
摘要： The distribution of solar irradiance on the absorbing surface of a typical integrated collector storage (ICS) system combined with reflector troughs is commonly studied by means of ray tracing techniques. A conceptually different alternative is offered by the method of the average number of reflections (ANR). In the present work, the latter is employed for the systematic optical study of realistic ICS models. In all cases, the solar devices consist of twin cylindrical storage tanks which are mounted on top of stationary asymmetrical CPC‐type reflectors. The emphasis of the current research is mainly placed on the evaluation of the ANR reliability for the calculation of the optical efficiency of the related twin‐tanked devices. Additionally, useful operational parameters, such as the optical performance of the proposed geometries, are also determined. The behavior of the tested ICS systems reveals that the optical efficiency may vary in the range of 0.75 to 0.91, exhibiting a strong dependence on the geometric parameters of the solar devices. The highest efficiency is achieved by the systems which combine large reflecting area and storage tanks in close proximity.
关键词： integrated collector storage (ICS) systems,optical study,average number of reflections,optical efficiency
更新于2025-09-23 15:19:57